Hot Sale Durability High Alumina Brick with Standard Size 230 X 114 X 65mm
Package Size 23.00cm * 11.40cm * 6.50cm Package Gross Weight 4.500kg Hot sale Durability High Alumina Brick with Standar
Basic Info.
Shape | Brick |
Material | Alumina Block |
Raw Material | Bauxite |
Color | White,Yellow |
Al2O3 Content (%) | 35-85% |
Application | Furnace Lining |
Transport Package | Wooden Pallets |
Specification | Standard Size 240*114*65mm |
Trademark | KRNC |
Origin | Henan, China |
HS Code | 6902200000 |
Production Capacity | 250000 Tons/Year |
Packaging & Delivery
Package Size 23.00cm * 11.40cm * 6.50cm Package Gross Weight 4.500kgProduct Description
Hot sale Durability High Alumina Brick with Standard Size 230 X 114 X 65mm Fire clay brick and high alumina brick are both belonging to Al2O3-SiO2 bricks. They can be divided into standard shapes and unique shapes. Standard shapes have dimensions conformed by most refractory manufacturers and are generally applicable to kilns or furnaces of the same types. Standard shapes are usually bricks that have a standard dimension of 9 × 4 1⁄2 × 2 1⁄2 inches (230 × 114 × 64 mm) and this dimension is called a "one brick equivalent". There are ranges of standard shapes of different sizes manufactured to produce walls, roofs, arches, tubes, circular apertures, etc. Special shapes are specifically made for specific locations within furnaces and for particular kilns or furnaces.Item/Grade | Fire Clay Brick | |||
SK-30 | SK-32 | SK-34 | SK-35 | |
Al2O3% (≥) | 30 | 35 | 38 | 45 |
Fe2O3% (≥) | 2.5 | 2.5 | 2 | 2 |
Refractoriness(SK) | 30 | 32 | 34 | 35 |
Refractoriness under load,0.2MPa, ºC (≥) | 1250 | 1300 | 1360 | 1420 |
Apparent porosity (%) | 22-26 | 20-24 | 20-22 | 18-20 |
Bulk density(g/cm3)) | 1.9-2.0 | 1.95-2.1 | 2.1-2.2 | 2.15-2.22 |
Cold crushing strength, MPa (≥) | 20 | 25 | 30 | 40 |
Item/Grade | High Alumina Brick | |||
SK-36 | SK-37 | SK-38 | SK-40 | |
Al2O3% (≥) | 55 | 65 | 70 | 75 |
Fe2O3% (≥) | 2 | 2 | 2 | 2 |
Refractoriness(SK) | 20-23 | 20-23 | 20-22 | 18-20 |
Refractoriness under load, 0.2MPa, ºC (≥) | 1250 | 1300 | 1360 | 1420 |
Operating temperature (ºC ) | 1400 | 1430 | 1480 | 1500 |
Bulk density(g/cm3) | 2.23 | 2.35 | 2.46 | 2.58 |
Cold crushing strength, MPa (≥) | 45 | 50 | 60 | 70 |
Unit weight (KG) | 3.8 | 4.0 | 4.2 | 4.4 |